Epoxy Systems and Phenolic Resins for Marine Composites

Composite materials are ideally suited to survive in the punishing marine environment. In response to customer demand, we supply easy-to-use formulated resin systems and back them with technical service to make sure our products work the way you need them to. Benefits include:

  • Robustness in harsh environmental conditions
  • High mechanical performance
  • Process-specific product lines
  • Easy-to-use formulated resin systems
  • Technical service excellence

Epoxy Resin SystemPerformance & FeaturesRemarks
Mix Ratio
(vol)
Tg
(°C/°F)
DIN EN ISO
11357
Pot Life
(min)1
DIN EN
14022
Mix
Viscosity
(at 25°C)
DIN 53019
/ ISO 3219
Infusion
Perfor-
mance
Exotherm-
icity
Tg
Develop-
ment
Crystalli-
zation
Stability
Resin Infusion
EPIKOTE™ Resin MGS™ RIMR 035c
EPIKURE™ Curing Agent MGS RIMH 0366 and 134
100:3480/176110-330250-280
 
 
 
 
 
 
 
 
 
 
 
 
  • Tailorable processing window
  • Low water absorption
  • DNV/GL approved
EPIKOTE Resin MGS RIMR 426
EPIKURE Curing Agents MGS RIMH 433-435
100:32100/21215-90220
 
 
 
 
 
 
 
 
 
 
 
 
  • Excellent ambient cure system
  • General purpose infusion system
  • Enables infusion at low ambient
    temperature

1) Pot life of 100g in a waterbath at 30°C

 
 
 
Good
 
 
 
Better
 
 
 
Best

Epoxy Resin SystemPerformance & FeaturesRemarks
Mix Ratio
(weight)
Tg
(°C/°F)
DIN EN ISO
11357
Pot Life
(min)1
DIN EN
14022
Crystalli-
zation
Stability
Process
Robustness
Ambient
Cure
Surface
Quality
Hand Lay-up
EPIKOTE Resin MGS LR 235
EPIKURE Curing Agents MGS LH 234 and 238
100:3595/20310-360
 
 
 
 
 
 
 
 
 
 
 
 
  • Reduced bleed out
  • Reduced exothermicity
  • DNV/GL approved
  • Improved laminate quality
  • Bio-based components

1) Pot life of 100g in a waterbath at 30°C

 
 
 
Good
 
 
 
Better
 
 
 
Best

Epoxy Resin SystemPerformance & FeaturesRemarks
Mix Ratio
(vol)
Tg
(°C/°F)
DIN EN ISO
11357
Time-to-
Handle(min)
Gap Filling
(mm)
Open TimeCrack
Resistance
Fatigue
Perfor-
mance
Ease of Use
Bonding Paste
EPIKOTE Resin BPR20/EPIKURE Curing Agent BPH20100:5090/19430-40<10
 
 
 
 
 
 
 
 
 
 
 
 
  • Multiple packaging options available
    including cartridge
  • Ambient cure
  • Good adhesion on unprepared surfaces
  • Composite-to-metal bonding
  • DNV/GL approved

1) Pot life of 100g in a waterbath at 30°C

 
 
 
Good
 
 
 
Better
 
 
 
Best

For more information, speak with a Hexion representative.

CELLOBOND™ Resins

For use in combination with Phenolic and Epoxy Resins, available Fire Resistant Gelcoat Cellobond™ ULF GC84-500_D for roll and spray application.


Resins gradeViscosity
at 25°C
[cP]
Solids
at 135°C
[%]
Water content [%]Free phenol [%]Free formaldehyde [%]SolventCommentsApplication
Cellobond™ J 2027 X01180-27072-7614-16< 10< 0.1WaterFree Formaldehyde <0,1%
Catalyst cured
excellent fire and smokes properties
RTM, VI, VARI
Cellobond™ J 2042 X01Thixotropic
(TI=1.7-3.8)
-14-16< 10< 0.1WaterFree Formaldehyde <0,1%
Catalyst cured
Excellent fire and smokes properties
Hand lamination
Cellobond™ULF PS90-206_D2000-300065-70max. 3.0max. 5< 0.1AlcoholFree Formaldehyde <0,1%
Excellent fire and smokes properties
Improved  Flexibility
Faster processing
Prepreg
Cellobond™ULF PS90-207_D325-42556.5-60.5max. 3.5max. 5< 0.1AlcoholFree Formaldehyde <0,1%
Excellent fire and smokes properties
Improved Flexibility
Faster processing
Prepreg
Cellobond™ULF PS90-601_D2500-300072-76max. 36.5-8.5< 0.1Alcohol Free Formaldehyde <0,1%
Improved fire and smokes properties and flexibility
Prepreg
Cellobond™ PF 1143 V50-7545-483-513-16max. 0.2AlcoholMil R-9299 certifiedHoneycomb
Cellobond™ SC1008P (EU)
Durite™ SC-1008 (USA)
180-30058-642-410-18max. 2AlcoholMil R-9299 / Mil-DTL-64154 certifiedPrepreg
Durite™ SC-830A200-30067-7220-257-9max. 1WaterMil-DTL-64154 certifiedHoneycomb