Bakelite® PF 8052

Description

Phenolic moulding compound, glass fibre-reinforced and inorganically filled, excellent heat resistance with respect to surface finish and mechanical properties

Application

Pan handles, heat-resistant up to 285°C, baking oven rollers

Typical Properties

Property Standard Value Unit Test Method
Additional Characteristic HT
Apparent Density Moulding Compound ISO 60 0.7 g/cm³
Ball Indentation Hardness H961/30 ISO 2039/P1 275 MPa
Charpy Impact Strength 23°C ISO 179-1 eU 6 kJ/m²
Charpy Notched Impact Strength 23°C ISO 179-1 eA 2 kJ/m²
Compression - Moulding shrinkage ISO 2577 0.3 %
Compression - Post shrinkage ISO 2577 0.1 %
Compressive Strength Test Specimen Flat Tested ISO 604 250 MPa
Density 23°C ISO 1183 1.5 g/cm³
Dissipation Factor 100 Hz IEC 60250 0
Electric Strength 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 IEC 60243-P1 0 kV/mm
Flammability UL 94 UL 94 0 Step/mm
Flexural Modulus ISO 178 8.5 MPa
Flexural Strength 2 mm/min ISO 178 90 MPa
Injection - Moulding Shrinkage ISO 2577 0.4 %
Injection - Post Shrinkage ISO 2577 0.1 %
Proof Tracking Index Test Liquid A IEC 60112 0 PTI
Relative Permittivity 100 Hz IEC 60250 0
Surface Resistivity IEC 60093 0 Ohm
Temp. of Deflection Under Load HDT C-8,0 MPa ISO 75-2 150 °C
Tensile Modulus 1mm/min, Elongatione1 0,05%; e2 0,25% ISO 527 - 1/2 8 MPa
Tensile Strength 5 mm/min ISO 527 - 1/2 55 MPa
Volume Resistivity IEC 60093 0 Ohm*cm
Water Absorption 24h / 23°C ISO 62 13 mg