Bakelite® PF 1110

Description

Phenolic moulding compound, inorganically filled, glass fibre reinforced, high heat resistance, very low coefficient of thermal expansion, highest resistance to pressure, high dimensional stability

Application

Motor vehicle engine attachments, insulating flanges, brake pistons, sensors, grinding disc centers, bearing parts, impellers, pulleys and pump parts

Typical Properties

Property Standard Value Unit Test Method
Additional Characteristic D, HT
Apparent Density ISO 60 0.8 g/cm³
Ball Indentation Hardness H961/30 ISO 2039/P1 0 MPa
Charpy Impact Strength 23°C ISO 179-1 eU 14 kJ/m²
Charpy Notched Impact Strength 23°C ISO 179-1 eU 4 kJ/m²
Compression - Moulding shrinkage ISO 2577 0 %
Compression - Post shrinkage ISO 2577 0 %
Compressive Strength Test Specimen Flat Tested ISO 604 275 MPa
Density 23°C ISO 1183 2.05 g/cm³
Dissipation Factor 100 Hz IEC 60250 0.05
Electric Strength 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 IEC 60243-P1 27.5 kV/mm
Flammability UL 94 UL 94 V-0 / 0,8mm Step/mm
Flexural Modulus ISO 178 25 MPa
Flexural Strength 2 mm/min ISO 178 240 MPa
Injection - Moulding Shrinkage ISO 2577 0.15 %
Injection - Post Shrinkage ISO 2577 0.03 %
Proof Tracking Index Test Liquid A IEC 60112 225 PTI
Relative Permittivity 100 Hz IEC 60250 6.5
Surface Resistivity IEC 60093 1E+11 Ohm
Temp. of Deflection Under Load HDT C-8,0 MPa ISO 75-2 195 °C
Tensile Modulus 1 mm/min ISO 527 - 1/2 26.000 MPa
Tensile Strength 5 mm/min ISO 527 - 1/2 120.000 MPa
Volume Resistivity IEC 60093 1E+12 Ohm*cm
Water Absorption 24h / 23°C ISO 62 7 mg