Bakelite® PF 2560

Description

Phenolic moulding compound, inorganically/organically filled, average heat resistance, high surface quality, lower water absorption than PF 31, minimal distortion, UL listed moulding compound 1.5 mm / V-1 (ALL), 3.0 mm / V-0 (ALL)

Application

Housings for domestic appliances, oven strips

Typical Properties

Property Standard Value Unit Test Method
Additional Characteristic A, EL, UL
Apparent Density ISO 60 0.75 g/cm³
Ball Indentation Hardness H961/30 ISO 2039/P1 350 MPa
Charpy Impact Strength 23°C ISO 179-1 eU 6 kJ/m²
Charpy Notched Impact Strength 23°C ISO 179-1 eA 1.6 kJ/m²
Compression - Moulding shrinkage ISO 2577 0 %
Compression - Post shrinkage ISO 2577 0 %
Compressive Strength Test Specimen Flat Tested ISO 604 250 MPa
Density 23°C ISO 1183 1.59 g/cm³
Dissipation Factor 100 Hz IEC 60250 0.2
Electric Strength 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 IEC 60243-P1 6 kV/mm
Flammability UL 94 UL 94 V-1/ 1,5mm (ALL), V-0 / 1,5mm (BK,NC) Step/mm
Flexural Modulus ISO 178 9000 MPa
Flexural Strength 2 mm/min ISO 178 90 MPa
Injection - Moulding Shrinkage ISO 2577 0.75 %
Injection - Post Shrinkage ISO 2577 0.4 %
Proof Tracking Index Test Liquid A IEC 60112 125 PTI
Relative Permittivity 100 Hz IEC 60250 14.5
Surface Resistivity IEC 60093 1E+10 Ohm
Temp. of Deflection Under Load HDT C-8,0 MPa ISO 75-2 115 °C
Tensile Modulus 1 mm/min ISO 527 - 1/2 9000 MPa
Tensile Strength 5 mm/min ISO 527 - 1/2 50 MPa
Volume Resistivity IEC 60093 1E+11 Ohm*cm
Water Absorption 24h / 23°C ISO 62 0 mg

 