Description

Polyester moulding compound, mainly organically filled, styrene free, processing shrinkage as for phenolic moulding compounds, nonflammable, high surface quality, UL listed moulding compound 1,5 mm / V-0 (ALL)

Application

Lamp housings, neon tubes end parts and bases, switch gears, watt hour meters housings and base plates

Typical Properties

Property Standard Value Unit Test Method
Apparent Density ISO 60 0,70 g/cm³
Ball Indentation Hardness H961/30 ISO 2039/P1 250 MPa
Charpy Impact Strength 23°C ISO 179-1 eU 7,5 kJ/m²
Charpy Notched Impact Strength 23°C ISO 179-1 eA 1,8 kJ/m²
Compression - Moulding shrinkage ISO 2577 0,6 %
Compression - Post shrinkage ISO 2577 0,25 %
Compressive Strength Test Specimen Flat Tested ISO 604 180 MPa
Density 23°C ISO 1183 1,72 g/cm³
Dissipation Factor 100 Hz, Following IEC 60250 0,02
Electric Strength 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 IEC 60243-P1 29,5 kV/mm
Flexural Modulus ISO 178 8000 MPa
Flexural Strength 2mm/min ISO 178 85 MPa
Injection - Moulding Shrinkage ISO 2577 0,75 %
Injection - Post Shrinkage ISO 2577 0,25 %
Proof Tracking Index Test Liquid A IEC 60112 29,5 PTI
Relative Permittivity 100 Hz, Following IEC 60250 5
Surface Resistivity Following IEC 60093 1,00E+11 Ohm
Temp. of Deflection Under Load HDT C-8,0 MPa ISO 75-2 75 °C
Tensile Modulus 1mm/min, Elongation e1 0,05%; e2 0,25% ISO 527 - 1/2 8500 MPa
Tensile Strength 5mm/min ISO 527 - 1/2 50 MPa
Volume Resistivity Following IEC 60093 1,00E+12 Ohm*cm
Water Absorption 24h / 23°C, Following ISO 62 70 mg