EPON™ Resin 1007F is a moderately high molecular weight solid epoxy resin derived from a liquid epoxy resin and bisphenol-A. This resin is used extensively as a vehicle in high performance industrial baking finishes. In these coatings the EPON Resin 1007F is usually reacted with urea formaldehyde or phenol-formaldehyde resins to develop the desired film properties. Coatings of this type exhibit outstanding flexibility and adhesion as well as exceptional resistance to chemicals and solvents. Some of the more important applications for EPON Resin 1007F/urea-formaldehyde or phenol formaldehyde coatings are linings for metal containers, appliance primers, metal furniture finishes and clear coatings for brass hardware and cosmetic cases. EPON Resin 1007F also finds application in powder coatings and may be used as a partial replacement for other EPON Resins in amine or polyamide cured two package coatings. In addition, this product can be reacted with vegetable oil acids and isocyanate curing agents to produce epoxy resin esters and urethane coatings, respectively.
Property | Standard | Value | Unit | Test Method |
---|---|---|---|---|
Color | 200 | Pt-Co | ASTM D1209 | |
Viscosity at 25°C | 50 - 100 | cP | ASTM D445 | |
Weight per Epoxide | 1700 - 2300 | g/eq | ASTM D1652 |
Property | Standard | Value | Unit | Test Method |
---|---|---|---|---|
Bulk Density | 36 - 40 | lbs/ft³ | ||
Esterification Equivalent Weight1 | 200 | |||
Flash Point Setaflash | 200 - 0 | °F | ASTM D3278 | |
Hydroxyl Content | 0.33 | |||
Melting Point | 120 - 130 | °C | ASTM D-3461 | |
Sodium Content | 2 | ppm | ||
Weight per Gallon at 20°C | 10.3 | lbs |