Phenolic moulding compound, mainly organically filled, standard moulding compound for normal stress, UL listed moulding compound 1.5 mm / V-1 (ALL), 3.0 mm / V-0 (ALL), standardized moulding compound
Mouldings of all kinds from screw caps to large casings, electrical installation material, handle casings (bars), pan handles, operating elements, toaster parts and pistons for braking power energizers, carbon brush holders, lamp casing parts, decor items, ashtrays
Property | Standard | Value | Unit | Test Method |
---|---|---|---|---|
Additional Characteristic | UL | |||
Apparent Density Moulding Compound | ISO 60 | 0.65 | g/cm³ | |
Ball Indentation Hardness H961/30 | ISO 2039/P1 | 300 | MPa | |
Charpy Impact Strength 23°C | ISO 179-1 eU | 7 | kJ/m² | |
Charpy Notched Impact Strength 23°C | ISO 179-1 eA | 1.5 | kJ/m² | |
Compression - Moulding shrinkage | ISO 2577 | 0.45 | % | |
Compression - Post shrinkage | ISO 2577 | 0.45 | % | |
Compressive Strength Test Specimen Flat Tested | ISO 604 | 250 | MPa | |
Density 23°C | ISO 1183 | 1.42 | g/cm³ | |
Dissipation Factor 100 Hz | IEC 60250 | .3 | ||
Electric Strength 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 | IEC 60243-P1 | 22.5 | kV/mm | |
Flammability UL 94 | UL 94 | V-1 / 1,5mm (ALL); V-0 / 3,0mm (ALL) | Step/mm | |
Flexural Modulus | ISO 178 | 7.5 | MPa | |
Flexural Strength 2 mm/min | ISO 178 | 95 | MPa | |
Injection - Moulding Shrinkage | ISO 2577 | 0.85 | % | |
Injection - Post Shrinkage | ISO 2577 | 0.55 | % | |
Proof Tracking Index Test Liquid A | IEC 60112 | 125 | PTI | |
Relative Permittivity 100 Hz | IEC 60250 | 11.0 | ||
Surface Resistivity | IEC 60093 | 1E+10 | Ohm | |
Temp. of Deflection Under Load HDT C-8,0 MPa | ISO 75-2 | 120 | °C | |
Tensile Modulus 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 | ISO 527 - 1/2 | 7.5 | MPa | |
Tensile Strength 5 mm/min | ISO 527 - 1/2 | 50 | MPa | |
Volume Resistivity | IEC 60093 | 1E+11 | Ohm*cm | |
Water Absorption 24h / 23°C | ISO 62 | 65 | mg |