Bakelite® PF 6501

Description

Phenolic moulding compound, inorganically filled, glass fibre reinforced, high dimensional stability at raised temperature, good media resistance, heat-resistant

Application

Thermally and dynamically highly stressed parts in automotive field, pulleys

Typical Properties

Property Standard Value Unit Test Method
Additional Characteristic D
Apparent Density Moulding Compound ISO 60 0.6 g/cm³
Ball Indentation Hardness H961/30 ISO 2039/P1 400 MPa
Charpy Impact Strength 23°C ISO 179-1 eU 12.5 kJ/m²
Charpy Notched Impact Strength 23°C ISO 179-1 eA 4.5 kJ/m²
Compression - Moulding shrinkage ISO 2577 0.2 %
Compression - Post shrinkage ISO 2577 0.1 %
Compressive Strength Test Specimen Flat Tested ISO 604 250 MPa
Density 23°C ISO 1183 1.6 g/cm³
Dissipation Factor 100 Hz IEC 60250 0.1
Electric Strength 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 IEC 60243-P1 33 kV/mm
Flammability UL 94 UL 94 0 Step/mm
Flexural Modulus ISO 178 12.5 MPa
Flexural Strength 2 mm/min ISO 178 175 MPa
Injection - Moulding Shrinkage ISO 2577 0.25 %
Injection - Post Shrinkage ISO 2577 0.1 %
Proof Tracking Index Test Liquid A IEC 60112 0 PTI
Relative Permittivity 100 Hz IEC 60250 6
Surface Resistivity IEC 60093 1E+10 Ohm
Temp. of Deflection Under Load HDT C-8,0 MPa ISO 75-2 170 °C
Tensile Modulus 1mm/min, Elongatione1 0,05%; e2 0,25% ISO 527 - 1/2 0 MPa
Tensile Strength 5 mm/min ISO 527 - 1/2 0 MPa
Volume Resistivity IEC 60093 1E+11 Ohm*cm
Water Absorption 24h / 23°C ISO 62 14 mg