Keripol RW 1411

Description

Polyester moulding compound, inorganically filled, glass fibre reinforced, styrene free, tracking resistance 600 V, good heat resistance, high viscosity flow characteristics

Application

H4 lampholders

Typical Properties

Property Standard Value Unit Test Method
Additional Characteristic D, HT
Apparent Density ISO 60 1,0 g/cm³
Ball Indentation Hardness H961/30 ISO 2039/P1 0 MPa
Charpy Impact Strength 23°C ISO 179-1 eU 5 kJ/m²
Charpy Notched Impact Strength 23°C ISO 179-1 eA 2 kJ/m²
Compression - Moulding shrinkage ISO 2577 0,1 %
Compression - Post shrinkage ISO 2577 -0,03 %
Compressive Strength Test Specimen Flat Tested ISO 604 0 MPa
Density 23°C ISO 1183 2,1 g/cm³
Dissipation Factor 100 Hz IEC 60250 0,008
Electric Strength 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 IEC 60243-P1 30 kV/mm
Flammability UL 94 ALL=all colours, BG=beige, BK=black, BN=brown, BL=blue, GN=green, GY=grey, NC=natural, OR=orange, RD=red, WT=white, YL=yellow UL 94 0 Step/mm
Flexural Modulus ISO 178 16500 MPa
Flexural Strength 2mm/min ISO 178 85 MPa
Injection - Moulding Shrinkage ISO 2577 0 %
Injection - Post Shrinkage ISO 2577 0 %
Proof Tracking Index Test Liquid A IEC 60112 600 PTI
Relative Permittivity 100 Hz IEC 60250 6
Surface Resistivity IEC 60093 1,00E+12 Ohm
Temp. of Deflection Under Load HDT C-8,0 MPa ISO 75-2 160 °C
Tensile Modulus 1mm/min, Elongation e1 0,05%; e2 0,25% ISO 527 - 1/2 MPa
Tensile Strength 5mm/min ISO 527 - 1/2 0 MPa
Volume Resistivity IEC 60093 1,00E+13 Ohm*cm
Water Absorption 24h / 23°C ISO 62 15 mg

 